Top substrate IR = 1 IR = 1.54+2e-03i 50.0.um thick (77.0.um optical) = 7.000 wave @ 11.0.um Bottom substrate IR = 1 "50.um Polyethylene Film; n = 1.54+0.002i" Plotting 1200 samples from 2.50.um :: 25.0.um (wavelengths) to "hdpe-const.eps" Column 1 average is 0.804463 Column 2 average is 0.0795029 Top substrate IR = 1 IR ~ 1.58+8.1e-04i~14.0.um thick (22.1.um optical) ~ 2.010 wave @ 11.0.um Bottom substrate IR = 1 "Polyethylene Card" Plotting 2000 samples from 2.50.um :: 25.0.um (wavenumbers) to "hdpe-card.eps" Column 1 average is 0.81712 Top substrate IR = 1 IR ~ 1.58+8.1e-04i~18.0.um thick (28.4.um optical) ~ 2.584 wave @ 11.0.um Bottom substrate IR = 1 "Polyethylene Card Absorption" Plotting 600 samples from 1.82.um :: 18.2.um (logarithmic) to "hdpe-card-absorb.eps" Column 1 average is 0.209682 Top substrate IR = 1 IR ~ 1.58+8.1e-04i 25.4.um thick (40.1.um optical) ~ 3.646 wave @ 11.0.um Bottom substrate IR = 1 "25.4.um HDPE" Plotting 800 samples from 2.35.um :: 15.2.um (logarithmic) with markers at 2.50.um 5.00.um 10.0.um to "hdpe-pe.eps" Column 1 average is 0.813177 Top substrate IR = 1 IR ~ 1.58+8.1e-04i 100.um thick ( 158.um optical) ~ 14.355 wave @ 11.0.um Bottom substrate IR = 1 "100.um HDPE" Plotting 1200 samples from 2.50.um :: 50.0.um (wavenumbers) to "hdpe-age-1.eps" Column 1 average is 0.738272 Top substrate IR = 1 IR ~ 1.58+1.4e-03i 100.um thick ( 158.um optical) ~ 14.355 wave @ 11.0.um Bottom substrate IR = 1 "100.um Polyethylene Film; variable n" Plotting 600 samples from 2.00.um :: 20.0.um (wavelengths) to "hdpe-L100.eps" Top substrate IR = 1 IR ~ 1.58+1.4e-03i~ 100.um thick ( 158.um optical) ~ 14.355 wave @ 11.0.um Bottom substrate IR = 1 "100.um Polyethylene Film; variable n" Plotting 600 samples from 2.00.um :: 20.0.um (wavelengths) to "hdpe-L100.eps" Column 1 average is 0.778088 Column 2 average is 0.0954639 Column 1 average is 0.774447 Column 2 average is 0.0995563 Top substrate IR = 1 IR ~ 1.58+8.1e-04i 32.0.um thick (50.5.um optical) ~ 4.593 wave @ 11.0.um Bottom substrate IR = 1 "Polyethylene FTIR" Plotting 1000 samples from 2.50.um :: 22.2.um (wavenumbers) to "hdpe-ftir.eps" Column 1 average is 0.792 Top substrate IR = 1 IR ~ 1.58+8.1e-04i~32.0.um thick (50.5.um optical) ~ 4.593 wave @ 11.0.um Bottom substrate IR = 1 "Polyethylene PAS" Plotting 1000 samples from 2.50.um :: 22.2.um (wavenumbers) to "hdpe-pas.eps" Column 1 average is 0.849191 Top substrate IR = 1 IR ~ 1.58+1.4e-03i 33.0.um thick (52.1.um optical) ~ 4.737 wave @ 11.0.um Bottom substrate IR = 1 "33.um Polyethylene Film; variable n" Plotting 600 samples from 2.00.um :: 20.0.um (wavelengths) to "hdpe-L33.eps" Top substrate IR = 1 IR ~ 1.58+1.4e-03i~33.0.um thick (52.1.um optical) ~ 4.737 wave @ 11.0.um Bottom substrate IR = 1 "33.um Polyethylene Film; variable n" Plotting 600 samples from 2.00.um :: 20.0.um (wavelengths) to "hdpe-L33.eps" Column 1 average is 0.852813 Column 2 average is 0.103125 Column 1 average is 0.848679 Column 2 average is 0.107439 Top substrate IR = 1 IR ~ ? 35.0.um thick Bottom substrate IR = 1 "35.um Polyethylene" Plotting 1000 samples from 2.50.um :: 25.0.um (wavenumbers) to "polyeth-35.eps" Top substrate IR = 1 IR ~ ? ~35.0.um thick Bottom substrate IR = 1 "35.um Polyethylene" Plotting 1000 samples from 2.50.um :: 25.0.um (wavenumbers) to "polyeth-35.eps" Column 1 average is 0.788974 Column 1 average is 0.782423 Top substrate IR = 1 IR ~ 1.58+8.1e-04i 50.0.um thick (78.9.um optical) ~ 7.177 wave @ 11.0.um Bottom substrate IR = 1 "50.um Polyethylene Film" Plotting 1200 samples from 500.nm :: 15.0.um (wavelengths) to "hdpe-50.eps" Column 1 average is 0.788292 Top substrate IR = 1 IR ~ 1.58+8.1e-04i~12.7.um thick (20.1.um optical) ~ 1.823 wave @ 11.0.um Bottom substrate IR = 1 "12.7.um High Density Polyethylene Film" Plotting 400 samples from 2.00.um :: 15.0.um (wavelengths) to "hdpe-12.7.eps" Column 1 average is 0.8476 Top substrate IR = 1 IR ~ 1.58+8.1e-04i 14.0.um thick (22.1.um optical) ~ 2.010 wave @ 11.0.um Bottom substrate IR = 1 "14.um Polyethylene Film" Plotting 400 samples from 4.50.um :: 26.0.um (wavelengths) to "hdpe-14.eps" Top substrate IR = 1 IR ~ 1.58+8.1e-04i 14.0.um thick (22.1.um optical) ~ 2.010 wave @ 11.0.um Bottom substrate IR = 1 "14.um Polyethylene Film" Plotting 400 samples from 4.50.um :: 26.0.um (wavelengths) to "hdpe-14.eps" Column 1 average is 0.893494 Column 1 average is 0.893494 Top substrate IR = 1 IR ~ 1.58+8.1e-04i 33.0.um thick (52.1.um optical) ~ 4.737 wave @ 11.0.um Bottom substrate IR = 1 "33.um High Density Polyethylene foil" Plotting 1200 samples from 2.00.um :: 20.0.um (wavelengths) to "hdpe-33.eps" Column 1 average is 0.839523 Column 2 average is 0.101756 Top substrate IR = 1 IR ~ 1.58+8.1e-04i~33.0.um thick (52.1.um optical) ~ 4.737 wave @ 11.0.um Bottom substrate IR = 1 "33.um High Density Polyethylene foil" Plotting 1200 samples from 2.00.um :: 20.0.um (wavelengths) to "hdpe-33ni.eps" Column 1 average is 0.835234 Column 2 average is 0.106066 Top substrate IR = 1 IR ~ 1.58+8.1e-04i~ 130.um thick ( 205.um optical) ~ 18.661 wave @ 11.0.um Bottom substrate IR = 1 "130.um Polyethylene Film" Plotting 1000 samples from 2.50.um :: 14.9.um (wavelengths) to "hdpe-130.eps" Column 1 average is 0.697458 Top substrate IR = 1 IR ~ ? ~33.0.um thick Bottom substrate IR = 1 "33.um Polyethylene" Plotting 200 samples from 147.nm :: 2.48.um (evs) to "pe-33.um.eps" Column 1 average is 0.562302